Lithium metal—seawater battery cells having protected lithium electrodes

ABSTRACT

Active metal and active metal intercalation electrode structures and battery cells having ionically conductive protective architecture including an active metal (e.g., lithium) conductive impervious layer separated from the electrode (anode) by a porous separator impregnated with a non-aqueous electrolyte (anolyte). This protective architecture prevents the active metal from deleterious reaction with the environment on the other (cathode) side of the impervious layer, which may include aqueous or non-aqueous liquid electrolytes (catholytes) and/or a variety electrochemically active materials, including liquid, solid and gaseous oxidizers. Safety additives and designs that facilitate manufacture are also provided.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 15/487,364, filed Apr. 13, 2017, now allowed, which is a continuation of U.S. patent application Ser. No. 15/150,231, filed May 9, 2016, now issued as U.S. Pat. No. 9,666,850 on May 30, 2017, which is a continuation of U.S. patent application Ser. No. 14/156,267, filed Jan. 15, 2014, now issued as U.S. Pat. No. 9,368,775 on Jun. 14, 2016, which claims priority to U.S. Provisional Patent Application No. 61/763,412 filed Feb. 11, 2003, titled PROTECTED LITHIUM ELECTRODES HAVING A POROUS ELECTROLYTE INTERLAYER AND BATTERY CELLS THEREOF; and is a continuation-in-part of U.S. patent application Ser. No. 13/929,653, filed Jun. 27, 2013, titled LITHIUM BATTERY HAVING A PROTECTED LITHIUM ELECTRODE AND AN IONIC LIQUID CATHOLYTE, now U.S. Pat. No. 8,828,580; which is a continuation of U.S. patent application Ser. No. 13/615,351, filed Sep. 13, 2012, titled PROTECTED LITHIUM ELECTRODES HAVING A POLYMER ELECTROLYTE INTERLAYER AND BATTERY CELLS THEREOF, now U.S. Pat. No. 8,501,339; which is a continuation of U.S. patent application Ser. No. 12/888,154, filed Sep. 22, 2010, titled PROTECTED ACTIVE METAL ELECTRODE AND BATTERY CELL WITH IONICALLY CONDUCTIVE PROTECTIVE ARCHITECTURE, now U.S. Pat. No. 8,293,398; which is a continuation of U.S. patent application Ser. No. 11/824,597, filed Jun. 28, 2007, titled PROTECTED ACTIVE METAL ELECTRODE AND BATTERY CELL STRUCTURES WITH NON-AQUEOUS INTERLAYER ARCHITECTURE, now U.S. Pat. No. 7,829,212; which is a divisional of U.S. patent application Ser. No. 10/824,944, filed Apr. 14, 2004, titled PROTECTED ACTIVE METAL ELECTRODE AND BATTERY CELL STRUCTURES WITH NON-AQUEOUS INTERLAYER ARCHITECTURE, now U.S. Pat. No. 7,282,295; which in turn claims priority to U.S. Provisional Patent Application No. 60/542,532 filed Feb. 6, 2004, titled PROTECTED ACTIVE METAL ELECTRODE AND BATTERY CELL STRUCTURES WITH NON-AQUEOUS INTERLAYER ARCHITECTURE; and U.S. Provisional Patent Application No. 60/548,231 filed Feb. 27, 2004, titled VARIATIONS ON PROTECTED ACTIVE METAL ELECTRODE AND BATTERY CELL STRUCTURES WITH NON-AQUEOUS INTERLAYER ARCHITECTURE.

Application Ser. No. 14/156,267 also claims the benefit of U.S. Provisional Patent Application No. 61/763,412 filed Feb. 11, 2013, titled PROTECTED LITHIUM ELECTRODES HAVING A POROUS ELECTROLYTE INTERLAYER AND BATTERY CELLS THEREOF.

The disclosures of all these prior applications are incorporated herein by reference in their entirety and for all purposes.

STATEMENT OF GOVERNMENT SUPPORT

This invention was made with Government support under Award No.: DE-AR0000349 awarded by the Advanced Research Projects Agency-Energy (ARPA-E), U.S. Department of Energy. The Government has certain rights in this invention.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The present invention relates generally to active metal electrochemical devices. More particularly, this invention relates to an active metal (e.g., alkali metals, such as lithium), active metal intercalation (e.g. lithium-carbon, carbon) and active metal alloys (e.g., lithium-tin) alloys or alloying metals (e.g., tin) electrochemical (e.g., electrode) structures and battery cells. The electrode structures have ionically conductive protective architecture including an active metal (e.g., lithium) conductive impervious layer separated from the electrode (anode) by a porous separator impregnated with a non-aqueous electrolyte. This protective architecture prevents the active metal from deleterious reaction with the environment on the other (cathode) side of the impervious layer, which may include aqueous, air or organic liquid electrolytes and/or electrochemically active materials.

2. Description of Related Art

The low equivalent weight of alkali metals, such as lithium, render them particularly attractive as a battery electrode component. Lithium provides greater energy per volume than the traditional battery standards, nickel and cadmium. Unfortunately, no rechargeable lithium metal batteries have yet succeeded in the market place.

The failure of rechargeable lithium metal batteries is largely due to cell cycling problems. On repeated charge and discharge cycles, lithium “dendrites” gradually grow out from the lithium metal electrode, through the electrolyte, and ultimately contact the positive electrode. This causes an internal short circuit in the battery, rendering the battery unusable after a relatively few cycles. While cycling, lithium electrodes may also grow “mossy” deposits that can dislodge from the negative electrode and thereby reduce the battery's capacity.

To address lithium's poor cycling behavior in liquid electrolyte systems, some researchers have proposed coating the electrolyte facing side of the lithium negative electrode with a “protective layer.” Such protective layer must conduct lithium ions, but at the same time prevent contact between the lithium electrode surface and the bulk electrolyte. Many techniques for applying protective layers have not succeeded.

Some contemplated lithium metal protective layers are formed in situ by reaction between lithium metal and compounds in the cell's electrolyte that contact the lithium. Most of these in situ films are grown by a controlled chemical reaction after the battery is assembled. Generally, such films have a porous morphology allowing some electrolyte to penetrate to the bare lithium metal surface. Thus, they fail to adequately protect the lithium electrode.

Various pre-formed lithium protective layers have been contemplated. For example, U.S. Pat. No. 5,314,765 (issued to Bates on May 24, 1994) describes an ex situ technique for fabricating a lithium electrode containing a thin layer of sputtered lithium phosphorus oxynitride (“LiPON”) or related material. LiPON is a glassy single ion conductor (conducts lithium ion) that has been studied as a potential electrolyte for solid state lithium microbatteries that are fabricated on silicon and used to power integrated circuits (See U.S. Pat. Nos. 5,597,660, 5,567,210, 5,338,625, and 5,512,147, all issued to Bates et al.).

Work in the present applicants' laboratories has developed technology for the use of glassy or amorphous protective layers, such as LiPON, in active metal battery electrodes. (See, for example, U.S. Pat. No. 6,025,094, issued Feb. 15, 2000, U.S. Pat. No. 6,402,795, issued Jun. 11, 2002, U.S. Pat. No. 6,214,061, issued Apr. 10, 2001 and U.S. Pat. No. 6,413,284, issued Jul. 2, 2002, all assigned to PolyPlus Battery Company).

Prior attempts to use lithium anodes in aqueous environments relied either on the use of very basic conditions such as use of concentrated aqueous KOH to slow down the corrosion of the Li electrode, or on the use of polymeric coatings on the Li electrode to impede the diffusion of water to the Li electrode surface. In all cases however, there was substantial reaction of the alkali metal electrode with water. In this regard, the prior art teaches that the use of aqueous cathodes or electrolytes with Li-metal anodes is not possible since the breakdown voltage for water is about 1.2 V and a Li/water cell can have a voltage of about 3.0 V. Direct contact between lithium metal and aqueous solutions results in violent parasitic chemical reaction and corrosion of the lithium electrode for no useful purpose. Thus, the focus of research in the lithium metal battery field has been squarely on the development of effective non-aqueous (mostly organic) electrolyte systems.

SUMMARY OF THE INVENTION

The present invention relates generally to active metal electrochemical devices. More particularly, this invention relates to an active metal (e.g., alkali metals, such as lithium), active metal intercalation (e.g. lithium-carbon, carbon) and active metal alloys (e.g., lithium-tin, lithium-silicon) alloys or alloying metals (e.g., tin, silicon) electrochemical (e.g., electrode) structures and battery cells. The electrochemical structures have ionically conductive protective architecture including an active metal (e.g., lithium) ion conductive substantially impervious layer separated from the electrode (anode) by a porous separator impregnated with a non-aqueous electrolyte (anolyte). This protective architecture prevents the active metal from deleterious reaction with the environment on the other (cathode) side of the impervious layer, which may include aqueous, air or organic liquid electrolytes (catholytes) and/or electrochemically active materials.

The separator layer of the protective architecture prevents deleterious reaction between the active metal (e.g., lithium) of the anode and the active metal ion conductive substantially impervious layer. Thus, the architecture effectively isolates (de-couples) the anode/anolyte from solvent, electrolyte processing and/or cathode environments, including such environments that are normally highly corrosive to Li or other active metals, and at the same time allows ion transport in and out of these potentially corrosive environments.

Various embodiments of the cells and cell structures of the present invention include active metal, active metal-ion, active metal alloying metal, and active metal intercalating anode materials protected with an ionically conductive protective architecture having a non-aqueous anolyte. These anodes may be combined in battery cells with a variety of possible cathode systems, including water, air, metal hydride and metal oxide cathodes and associated catholyte systems, in particular aqueous catholyte systems.

Safety additives may also be incorporated into the structures and cells of the present invention for the case where the substantially impervious layer of the protective architecture (e.g., a glass or glass-ceramic membrane) cracks or otherwise breaks down and allows the aggressive catholyte to enter and approach the lithium electrode. The non-aqueous interlayer architecture can incorporate a gelling/polymerizing agent that, when in contact with the reactive catholyte, leads to the formation of an impervious polymer on the lithium surface. For example, the anolyte may include a monomer for a polymer that is insoluble or minimally soluble in water, for example dioxolane (Diox)/polydioxaloane and the catholyte may include a polymerization initiator for the monomer, for example, a protonic acid.

In addition, the structures and cells of the present invention may take any suitable form. One advantageous form that facilitates fabrication is a tubular form.

In one aspect, the invention pertains to an electrochemical cell structure. The structure includes an anode composed of an active metal, active metal-ion, active metal alloy, active metal alloying metal or active metal intercalating material. The anode has an ionically conductive protective architecture on its surface. The architecture includes an active metal ion conducting separator layer that has a non-aqueous anolyte and is chemically compatible with the active metal and in contact with the anode, and a substantially impervious ionically conductive layer chemically compatible with the separator layer and aqueous environments and in contact with the separator layer. The separator layer may be, a semi-permeable membrane impregnated with an organic anolyte, for example, a micro-porous polymer impregnated with a liquid or gel phase anolyte. Such an electrochemical (electrode) structure may be paired with a cathode system, including an aqueous cathode system, to form battery cells in accordance with the present invention.

The structures and battery cells incorporating the structures of the present invention may have various configurations, including prismatic and cylindrical, and compositions, including active metal ion, alloy and intercalation anodes, aqueous, water, air, metal hydride and metal oxide cathodes, and aqueous, organic or ionic liquid catholytes; electrolyte (anolyte and/or catholyte) compositions to enhance the safety and/or performance of the cells; and fabrication techniques.

These and other features of the invention are further described and exemplified in the detailed description below.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic illustration of an electrochemical structure cell incorporating an ionically conductive protective interlayer architecture in accordance with the present invention.

FIG. 2 is a schematic illustration of a battery cell incorporating an ionically conductive protective interlayer architecture in accordance with the present invention.

FIGS. 3A-C illustrate embodiments of battery cells in accordance with the present invention that use a tubular protected anode design.

FIGS. 4-6 are plots of data illustrating the performance of various cells incorporating anodes with ionically conductive protective interlayer architecture in accordance with the present invention.

FIG. 7 illustrates a Li/water battery and hydrogen generator for a fuel cell in accordance with one embodiment of the present invention.

DETAILED DESCRIPTION OF SPECIFIC EMBODIMENTS

Reference will now be made in detail to specific embodiments of the invention. Examples of the specific embodiments are illustrated in the accompanying drawings. While the invention will be described in conjunction with these specific embodiments, it will be understood that it is not intended to limit the invention to such specific embodiments. On the contrary, it is intended to cover alternatives, modifications, and equivalents as may be included within the spirit and scope of the invention as defined by the appended claims. In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention. The present invention may be practiced without some or all of these specific details. In other instances, well known process operations have not been described in detail so as to not unnecessarily obscure the present invention.

When used in combination with “comprising,” “a method comprising,” “a device comprising” or similar language in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural reference unless the context clearly dictates otherwise. Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood to one of ordinary skill in the art to which this invention belongs.

Introduction

Active metals are highly reactive in ambient conditions and can benefit from a barrier layer when used as electrodes. They are generally alkali metals such (e.g., lithium, sodium or potassium), alkaline earth metals (e.g., calcium or magnesium), and/or certain transitional metals (e.g., zinc), and/or alloys of two or more of these. The following active metals may be used: alkali metals (e.g., Li, Na, K), alkaline earth metals (e.g., Ca, Mg, Ba), or binary or ternary alkali metal alloys with Ca, Mg, Sn, Ag, Zn, Bi, Al, Cd, Ga, In. Preferred alloys include lithium aluminum alloys, lithium silicon alloys, lithium tin alloys, lithium silver alloys, and sodium lead alloys (e.g., Na₄Pb). A preferred active metal electrode is composed of lithium.

The low equivalent weight of alkali metals, such as lithium, render them particularly attractive as a battery electrode component. Lithium provides greater energy per volume than the traditional battery standards, nickel and cadmium. However, lithium metal or compounds incorporating lithium with a potential near that (e.g., within about a volt) of lithium metal, such as lithium alloy and lithium-ion (lithium intercalation) anode materials, are highly reactive to many potentially attractive electrolyte and cathode materials. This invention describes the use of a non-aqueous electrolyte interlayer architecture to isolate an active metal (e.g., alkali metal, such as lithium), active metal alloy or active metal-ion electrode (usually the anode of a battery cell) from ambient and/or the cathode side of the cell. The architecture includes an active metal ion conducting separator layer with a non-aqueous anolyte (i.e., electrolyte about the anode), the separator layer being chemically compatible with the active metal and in contact with the anode, and a substantially impervious ionically conductive layer chemically compatible with the separator layer and aqueous environments and in contact with the separator layer. The non-aqueous electrolyte interlayer architecture effectively isolates (de-couples) the anode from ambient and/or cathode, including catholyte (i.e., electrolyte about the cathode) environments, including such environments that are normally highly corrosive to Li or other active metals, and at the same time allows ion transport in and out of these potentially corrosive environments. In this way, a great degree of flexibility is permitted the other components of an electrochemical device, such as a battery cell, made with the architecture. Isolation of the anode from other components of a battery cell or other electrochemical cell in this way allows the use of virtually any solvent, electrolyte and/or cathode material in conjunction with the anode. Also, optimization of electrolytes or cathode-side solvent systems may be done without impacting anode stability or performance.

There are a variety of applications that could benefit from the use of aqueous solutions, including water and water-based electrolytes, air, and other materials reactive to lithium and other active metals, including organic solvents/electrolytes and ionic liquids, on the cathode side of the cell with an active (e.g., alkali, e.g., lithium) metal or active metal intercalation (e.g., lithium alloy or lithium-ion) anode in a battery cell.

The use of lithium intercalation electrode materials like lithium-carbon and lithium alloy anodes (e.g., those based on Sn and Si), and combinations thereof, rather than lithium metal, for the anode can also provide beneficial battery characteristics. First of all, it allows the achievement of prolonged cycle life of the battery without risk of formation of lithium metal dendrites that can grow from the Li surface to the membrane surface causing the membrane's deterioration. Also, the use of lithium-carbon and lithium alloy anodes in some embodiments of the present invention instead of lithium metal anode can significantly improve a battery's safety because it avoids formation of highly reactive “mossy” lithium during cycling.

The present invention describes a protected active metal, alloy or intercalation electrode that enables very high energy density lithium batteries such as those using aqueous electrolytes or other electrolytes that would otherwise adversely react with lithium metal, for example. Examples of such high energy battery couples are lithium-air, lithium-water lithium-metal hydride, lithium-metal oxide, and the lithium alloy and lithium-ion variants of these. The cells of the invention may incorporate additional components in their electrolytes (anolytes and catholytes) to enhance cell safety, and may have a variety of configurations, including planar and tubular/cylindrical.

Non-Aqueous Interlayer Architecture

The non-aqueous interlayer architecture of the present invention is provided in an electrochemical cell structure, the structure having an anode composed of a material selected from the group consisting of active metal, active metal-ion, active metal alloy, active metal alloying and active metal intercalating material, and an ionically conductive protective architecture on a first surface of the anode. The architecture is composed of an active metal ion conducting separator layer with a non-aqueous anolyte, the separator layer being chemically compatible with the active metal and in contact with the anode, and a substantially impervious ionically conductive layer chemically compatible with the separator layer and aqueous environments and in contact with the separator layer. The separator layer may include a semi-permeable membrane, for example, a micro-porous polymer, such as are available from Celgard, Inc. Charlotte, N.C., impregnated with an organic anolyte.

In some embodiments, the porous separator layer is flexible. For instance the separator may be a porous polymeric material layer, such as a porous polyolefin (e.g., polyethyelenes or polypropylenes), porous polytetraflouroethylene layer (e.g., expanded PTFE), porous polyethylene terepthalate (PET) or some combination thereof such as a polyolefin multi-layer (e.g., a tri-layer) or a multi-layer of a porous PET or PTFE layer combined (e.g., by lamination to another layer or some other means of adhering the layers such as using a porous adhesives or chemical dissolution bonding) with a porous polyolefin layer to provide enhanced chemical compatibility in contact with lithium metal (e.g., a bi-layer where the polyolefin layer contacts the lithium) or the PTFE layer or PET layer may be sandwiched between two different porous polymer layers (e.g., between two polyolefin layers). The porous polymer layers may be processed using dry or wet methods, as are known in the battery separator arts. In the dry process, the film can be stretched to introduce micropores. The porous polymer layer may further be a nonwoven film or coating, which is processed from polymeric fibers into a film or coating.

The porous polymeric separator material layer is not limited to polyolefins, PTFE, or PET specifically but is understood to include all types of polymers which can be fabricated into a porous material layer including polyvinylidene fluoride (PVdF), polycarbonates, cellulosics, polyurethanes, polyesters, polyethers, polyacrylates, copolyether esters, copolyether amides, polyethyelene (PE), polypropylene (PP), polyacrylates, copolyether esters, copolyether amides, chitosn, and fluoropolymers generally.

Suitable fluoropolymers include expanded PTFE as taught in U.S. Pat. No. 3,953,566, which is hereby incorporated by reference for the purpose of disclosing this composition and methods for its fabrication and use. For instance, and as described above, to stabilize the porous PTFE membrane for direct contact with lithium, the PTFE layer may be sandwiched on one or both sides by a polymer layer of different composition, e.g., a polyolefin.

In various embodiments, the porous separator serving as interlayer may be a porous polymer layer or multilayer devoid of other material additives, or in other embodiments the separator layer may be a composite of a polymer (e.g., serving as the base material layer) and a second material such as a ceramic, for example a metal oxide, (e.g., ceramic metal oxide particles) disposed in pores of the polymer layer or a porous ceramic coating or thin porous ceramic film disposed on one or both polymer surface (e.g., sandwiching the polymer layer). For instance, a nano-porous ceramic film may be used. In some embodiments, the ceramic (be it a particle or film) is non-conductive to lithium ions and in other embodiments the ceramic is a lithium ion conductor. Suitable ceramic materials which may be used as a ceramic particle in the pores of a porous layer, typically a polymeric layer, serving as the base layer of the separator include metal oxides generally, and in particular the following: alumina (e.g., Al₂O₃), magnesia (e.g., MgO), LiAlO₂, lithium oxide, titanium oxide, magnesium oxide, aluminum oxide, zirconia (i.e., zirconium oxide), hafnium oxide, iron oxide, silica, barium titanate, and yttrium oxide. Other ceramic materials which are conductive of lithium ions and may be used as a ceramic particle or porous ceramic film include lithium titanium phosphates and the like as well as lithium ion conducting garnets, as described in more detail below.

Other particularly suitable materials as a ceramic particle or ceramic film or coating are lithium ion conducting oxides having a garnet like structures. These include Li₆BaLa₂Ta₂O₁₂; Li₇La₃Zr₂O₁₂, Li₅La₃Nb₂O₁₂, Li₅La₃M₂O₁₂ (M=Nb, Ta)Li_(7+x)A_(x)La_(3-x)Zr₂O₁₂ where A may be Zn. These materials and methods for making them are described in U.S. Patent Application Pub. No.: 2007/0148533 (application Ser. No. 10/591,714) and is hereby incorporated by reference for disclosure of these materials and methods for their making and use, and suitable garnet like structures, described, for example, in International Patent Application Pub. No.: WO/2009/003695, which is hereby incorporated by reference for disclosure of these materials and methods for their making and use. Suitable ceramic active metal ion conductors are described, for example, in U.S. Pat. No. 4,985,317 to Adachi et al., incorporated by reference herein for disclosure of these materials and methods for their making and use. LiM₂(PO₄)₃ where M may be Ti, Zr, Hf, Ge and related compositions such as those into which certain ion substitutions are made including Li_(1+x)Ti_(2-x)Al_(x)(PO₄)₃ and the like which are known in the lithium battery arts.

In various embodiments, the ceramic particle or porous ceramic film may be composed in whole or in part of lithium ion conductive materials which are suitable for use herein as the lithium ion conducting material of the substantially impervious membrane layer, and which are described in more detail below in the section on the second material layer (i.e., the substantially impervious layer). In other embodiments the aforementioned porous ceramic film or coating may be sandwiched between two porous polymeric layers.

While the porous separators described herein above are generally flexible, for instance having an elastic modulus (i.e., Young's modulus) in the range of less than 10 GPa, the invention is not so limited, and it is contemplated that rigid porous material layers may also serve as an interlayer (e.g., those having an elastic modulus greater than 10 GPa such). Such rigid layers include porous ceramic layers, porous metal layers, porous carbon foam layers and porous glass layers and which optionally may serve as a layer on the surface of a porous polymer layer, or porous polymer layer may be coated on the surface of the ceramic, metal or glass layer and thereon serve to provide some stability in contact with lithium metal (e.g., the surface layer a polyolefin), or the porous rigid layer (be it a polycrystalline metal oxide (e.g., a ceramic) or glass, or metal, may be sandwiched between two porous polymer layers. For instance a porous ceramic layer of alumina such as anodized alumina may be used.

In some embodiments, the ceramic particles are conductive of alkali metal ions, or conductive of electrons or otherwise insulating or semiconducting. In some embodiments, the particles may be nano particles. In some embodiments, the ceramic particles or ceramic layers may be reactive to lithium metal in contact, and thereby serve as a getter for shorting dendrites which may grow as a result of cell cycling. Suitable reactive ceramic layers include intercalation materials which may in contact with lithium metal reduce and intercalate lithium ions. Such intercalation materials are known in the lithium ion battery art and include titanium, tungsten, cobalt, and manganese oxides and the like.

In some embodiments, the porous separator layer has a polymeric base layer impregnated with a lithium ion conductive ceramic component, typically in particle form.

In some embodiments, the separator layer may be a composite of a porous polymeric base layer having ceramic filler particles disposed in pores of the base layer and further comprising a polymer capable of swelling or being gelled by a liquid electrolyte and thus serving in the separator as a gel material. Other materials which may be incorporated in the separator include ion exchange resin like materials, such as ion exchange polymeric materials, typically having functional groups that provide ion exchange properties, such as carboxylic, sulfonic and phosphonic groups. Suitable gel materials are known in the lithium battery art, and include copolymers of vinylidene fluoride with hexafluoropropylene (PVDF-HFP), poly(methyl methacrylate (PMMA), poly(acrylonitrile) (PAN) and polyethyelene oxide (PEO)

In the aforementioned embodiments, the separator layer may be further impregnated with a gelling agent, which is typically a polymer material capable of being swelled by the liquid electrolyte which is incorporated therein.

Material layers suitable for use herein as an interlayer component in the instant protected electrodes include those described in U.S. Pub. No.: 2012/0169016 to Hisano et al., published Jul. 5, 2012; U.S. Pat. No. 6,242,135 to Mushiake, U.S. Pat. Nos. 3,953,566; 4,187,390; 4,539,256; 4,429,000; 4,726,989; 4,100,238; 3,679,540, all of which are hereby incorporated by reference for disclosure of these materials, as well as those manufactured by Celgard LLC (e.g., PE, PP and PP/PE/PP), Asahi Kasei chemicals (e.g., Hipore); Entek Membranes (e.g., Separion), ExxonMobil/Tonen, SK Energy, Evonik, and DuPont (e.g., the Energain). Other suitable material layers which may serve herein as an interlayer include those which are described by S. S. Zhang in an article published in the Journal of Power of Sources 164 (2007) 351-364.

In yet other embodiments, the porous interlayer may include or be composed of an inorganic matrix material such as a porous layer composed of inorganic fibers, such as glass and/or ceramic fibers; the layer being thin (e.g., less than 50 um) or thick. In embodiments wherein the glass or ceramic fiber contacts the active metal anode, the composition of the fiber should be chemically compatible with the active metal anode; e.g., for embodiments wherein the glass or ceramic fiber contacts the lithium metal anode layer. For instance, a glass or ceramic mat is contemplated for use herein as an interlayer. Glass mats are known for their use as battery separators, especially for lead acid batteries (e.g., an AGM separator). AGM stands for absorptive glass mat and it generally a non-woven fabric made with glass microfibers.

In addition to microporous separator layers, non-woven fabric type separators may be used as an interlayer or interlayer component herein, including those described in U.S. Pat. No. 5,002,843 to Cieslak, which discloses aramid fibers in a non-woven mat format, and is hereby incorporated by reference. Other non-woven fabric type separators may be composed of glass or other inorganic or organic (e.g., polymeric fiber) fiber like materials. For instance, this may include non-woven polyesters and the like. In various embodiments the interlayer is a solid polymer electrolyte such as polyethylene oxide (PEO) and derivatives and blends thereof having a lithium salt (e.g., Li-TFSI) dissolved therein. These include blends such as block co-polymers of e.g., polystyrene (PS)—block-polyethylene oxide-block-polystyrene copolymers. Polymers based on block copolymers of PS and PEO are disclosed in U.S. patent application Ser. No. 12/225,934 and other useful compositions are disclosed in US Patent Publication No.: 20130066025, US Patent Publication No.: 20110318648 and US Patent Publication No.: 20130273419. Suitable lithium salts for the solid polymer anolyte interlayer, which are also suitable for anolytes based on various non-aqueous liquid solvents, include lithium trifluoromethansulfonate (LiCF₃SO₃), lithium bis(trifluoromethanesulfonimidate) (Li(CF₃SO₂)₂N); lithium bis(trifluoromethanesulfonimide) (Li(C₂F₅SO₂)₂N, lithium perchlorate (LiClO₄), and lithium bis(oxalato)borate (LiB(C₂O₄)₂). The solid polymer electrolyte may be modified by adding a plasticizer such as succinonitrile, polysquarate, EC, PC or some combination thereof, which reduces crystallization and thus generally increases conductivity, especially near room temperature.

The protective architecture of this invention incorporates a substantially impervious layer of an active metal ion conducting glass or glass-ceramic (e.g., a lithium ion conductive glass-ceramic (LIC-GC)) that has high active metal ion conductivity and stability to aggressive electrolytes that vigorously react with lithium metal, for example) such as aqueous electrolytes. Suitable materials are substantially impervious, ionically conductive and chemically compatible with aqueous electrolytes or other electrolyte (catholyte) and/or cathode materials that would otherwise adversely react with lithium metal, for example. Such glass or glass-ceramic materials are substantially gap-free, non-swellable and are inherently ionically conductive. That is, they do not depend on the presence of a liquid electrolyte or other agent for their ionically conductive properties. They also have high ionic conductivity, at least 10⁻⁷ S/cm, generally at least 10⁻⁶ S/cm, for example at least 10⁻⁵ S/CM to 10⁻⁴ S/cm, and as high as 10⁻³ S/cm or higher so that the overall ionic conductivity of the multi-layer protective structure is at least 10⁻⁷ S/cm and as high as 10⁻³ S/cm or higher. The thickness of the layer is preferably about 0.1 to 1000 microns, or, where the ionic conductivity of the layer is about 10⁻⁷ S/cm, about 0.25 to 1 micron, or, where the ionic conductivity of the layer is between about 10⁻⁴ about 10⁻³ S/cm, about 10 to 1000 microns, preferably between 1 and 500 microns, and more preferably between 10 and 100 microns, for example 20 microns.

Suitable examples of suitable substantially impervious lithium ion conducting layers include glassy or amorphous metal ion conductors, such as a phosphorus-based glass, oxide-based glass, phosphorus-oxynitride-based glass, sulpher-based glass, oxide/sulfide based glass, selenide based glass, gallium based glass, germanium-based glass or boracite glass (such as are described D. P. Button et al., Solid State Ionics, Vols. 9-10, Part 1, 585-592 (December 1983); ceramic active metal ion conductors, such as lithium beta-alumina, sodium beta-alumina, Li superionic conductor (LISICON), Na superionic conductor (NASICON), and the like; or glass-ceramic active metal ion conductors. Specific examples include LiPON, Li₃PO₄.Li₂S.SiS₂, Li₂S.GeS₂.Ga₂S₃, Li₂O.11Al₂O₃, Na₂O.11Al₂O₃, (Na, Li)_(1+x)Ti_(2-x)Al_(x)(PO₄)₃ (0.6≤x≤0.9) and crystallographically related structures, Na₃Zr₂Si₂PO₁₂, Li₃Zr₂Si₂PO₁₂, Na₅ZrP₃O₁₂, Na₅TiP₃O₁₂, Na₃Fe₂P₃O₁₂, Na₄NbP₃O₁₂, Li₅ZrP₃O₁₂, Li₅TiP₃O₁₂, Li₃Fe₂P₃O₁₂ and Li₄NbP₃O₁₂, and combinations thereof, optionally sintered or melted. Suitable ceramic ion active metal ion conductors are described, for example, in U.S. Pat. No. 4,985,317 to Adachi et al., incorporated by reference herein in its entirety and for all purposes.

A particularly suitable glass-ceramic material for the substantially impervious layer of the protective architecture is a lithium ion conductive glass-ceramic having the following composition:

Composition mol % P₂O₅ 26-55%  SiO₂ 0-15% GeO₂ + TiO₂ 25-50%  in which GeO₂ 0-50% TiO₂ 0-50% ZrO₂ 0-10% M₂O₃ 0-10% Al₂O₃ 0-15% Ga₂O₃ 0-15% Li₂O 3-25% and containing a predominant crystalline phase composed of Li_(1+x)(M,Al,Ga)_(x)(Ge_(1-y)Ti_(y))_(2-x)(PO₄)₃ where X≤0.8 and 0≤Y≤1.0, and where M is an element selected from the group consisting of Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm and Yb, and/or Li_(1+x+y)Q_(x)Ti_(2-x)Si_(y)P_(3-y)O₁₂ where 0<X≤0.4 and 0<Y≤0.6, and where Q is Al or Ga. The glass-ceramics are obtained by melting raw materials to a melt, casting the melt to a glass and subjecting the glass to a heat treatment. Such materials are available from OHARA Corporation, Japan and are further described in U.S. Pat. Nos. 5,702,995, 6,030,909, 6,315,881 and 6,485,622, incorporated herein by reference for disclosure of these materials and methods of making them.

Such lithium ion conductive substantially impervious layers and techniques for their fabrication and incorporation in battery calls are described in U.S. Provisional Patent Application No. 60/418,899, filed Oct. 15, 2002, titled IONICALLY CONDUCTIVE COMPOSITES FOR PROTECTION OF ANODES AND ELECTROLYTES, its corresponding U.S. patent application Ser. No. 10/686,189 (Attorney Docket No. PLUSP027), filed Oct. 14, 2003, and titled IONICALLY CONDUCTIVE COMPOSITES FOR PROTECTION OF ACTIVE METAL ANODES, U.S. patent application Ser. No. 10/731,771 (Attorney Docket No. PLUSP027X1), filed Dec. 5, 2003, and titled IONICALLY CONDUCTIVE COMPOSITES FOR PROTECTION OF ACTIVE METAL ANODES, and U.S. patent application Ser. No. 10/772,228 (Attorney Docket No. PLUSP039), filed Feb. 3, 2004, and titled IONICALLY CONDUCTIVE MEMBRANES FOR PROTECTION OF ACTIVE METAL ANODES AND BATTERY CELLS. These applications are incorporated by reference herein in their entirety for all purposes.

Another particularly suitable material for the second layer of the protective composite is a lithium ion conducting oxide having a garnet like structure. These include Li₆BaLa₂Ta₂O₁₂; Li₇La₃Zr₂O₁₂, Li₅La₃Nb₂O₁₂, Li₅La₃M₂O₁₂ (M=Nb, Ta)Li_(7+x)A_(x)La_(3-x)Zr₂O₁₂ where A may be Zn. These materials and methods for making them are described in U.S. Patent Application Pub. No.: 2007/0148533 (Appl. Ser. No. 10/591,714) and is hereby incorporated by reference, and suitable garnet like structures, are described in International Patent Application Pub. No.: WO/2009/003695 which is hereby incorporated by reference.

A critical limitation in the use of these highly conductive glasses and glass-ceramics in lithium (or other active metal or active metal intercalation) batteries is their reactivity to lithium metal or compounds incorporating lithium with a potential near that (e.g., within about a volt) of lithium metal. The non-aqueous electrolyte interlayer of the present invention isolates the lithium (for example) electrode from reacting with the glass or glass-ceramic membrane. The non-aqueous interlayer may have a semi-permeable membrane, such as a Celgard micro-porous separator, to prevent mechanical contact of the lithium electrode to the glass or glass-ceramic membrane. The membrane is impregnated with organic liquid electrolyte (anolyte) with solvents such as ethylene carbonate (EC), propylene carbonate (PC), 1,2-dimethoxy ethane (DME), 1,3-dioxolane (DIOX), or various ethers, glymes, lactones, sulfones, sulfolane, or mixtures thereof. It may also or alternatively have a polymer electrolyte, a gel-type electrolyte, or a combination of these. The important criteria are that the lithium electrode is stable in the non-aqueous anolyte, the non-aqueous anolyte is sufficiently conductive to Li⁺ ions, the lithium electrode does not directly contact the glass or glass-ceramic membrane, and the entire assembly allows lithium ions to pass through the glass or glass-ceramic membrane.

In various embodiments the liquid impermeable solid electrolyte membrane (i.e., the substantially impervious layer) may be a glass, glass-ceramic or ceramic membrane composed in whole or in part of an active metal ion conducting solid-state electrolyte material. For instance, the membrane fabricated by sintering a pellet or tape cast layer of said solid-state electrolyte material, including sintering of a tape cast glass material that in the process of densification during sintering crystallizes to a highly conductive phase.

Particularly suitable solid-state electrolyte materials include the following:

(i) garnet like compounds as described in PCT Patent Application WO 2013/010692 having Robert Bosch GMBH as applicant and inventors Eisele, Koehler, Hinderberger, Logeat, and Kozinsky and which is herein incorporated by reference:

-   -   Li_(n)[A_((3-a′-a″))A′_((a′))A″_((a″))][B_((2-b′-b″))B′_((b′))B″_((b″))][C′_((c′))C″_((c″)])]O₁₂         wherein     -   A represents at least one element selected from the group         consisting of La, Y, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm and         Yb;     -   A′ represents at least one element selected from the group         consisting of Ca, Sr, and Ba;     -   A″ represents at least one element selected from the group         consisting of Na and K;     -   with 0≤a′<2 and 0≤a″<1     -   B represents at least one element selected from the group         consisting of Zr, Hf, and Sn;     -   B′ represents at least one element selected from the group         consisting of Ta, Nb, Sb, and Bi;     -   B″ represents at least one element selected from the group         consisting of Te, W, and Mo     -   with 0≤b′≤2 and 0≤b″≤2;     -   C′ represents at least one element selected from the group         consisting of Al and Ga;     -   C″ represents at least one element selected from the group         consisting of Si and Ge;     -   with 0≤c′≤0.5 and 0≤c″≤0.4     -   and n=7+a′+2a″−b′−2b″−3c′−4c″ and 5.5≤n≤6.875 (or 5≤n≤7).     -   Particular examples include but are not limited to:         Li_(6.875)La₃Ta_(0.125)Zr_(1.875)O₁₂;         Li_(6.75)La₃Ta_(0.25)Zr_(1.75)O₁₂;         Li_(6.5)La₃Ta_(0.5)Zr_(1.5)O₁₂;         Li_(6.25)La₃Ta_(0.75)Zr_(1.25)O₁₂; Li₆La₃TaZrO₁₂;         Li_(5.5)La₃Ta_(1.5)Zr_(0.5)O₁₂; Al_(0.1)Li_(6.7)La₃Zr₂O₁₂;         Al_(0.17)Li_(6.49)La₃Zr₂O₁₂; Al_(0.23)Li_(6.31)La₃Zr₂O₁₂;         Al_(0.29)Li_(6.13)La₃Zr₂O₁₂; Al_(0.35)Li_(5.95)La₃Zr₂O₁₂;         Al_(0.3)Li_(5.85)Sr_(0.25) La_(2.75)Nb_(0.5)Zr_(1.5)O₁₂;         Si_(0.2)Li_(6.2)La₃Zr₂O₁₂         (ii) garnet like compounds as described in U.S. Patent         Application Pub. No.: 2011/0244337 having Kabushiki Kaisha         Toyota Chuo Kenkyusho as assignee and inventors Ohta, Kobayashi,         Asaoka, Asai, and which is herein incorporated by reference:     -   Li_(5+x)La₃(Zr_(x),A_(2-x))O₁₂ wherein     -   A is at least one selected from the group consisting of Sc, Ti,         V, Y, Nb, Hf, Ta, Al, Si, Ga, Ge, and Sn and X satisfies the         inequality 1.4≤X<2; or     -   A is one obtained by substituting an element having an ionic         radius different from that of Zr for Zr sites in a garnet type         lithium ion conducting oxide represented by the formula         Li₇La₃Zr₂O₁₂.         (iii) garnet like compounds as described in U.S. Pat. No.         8,092,941 having Werner Weppner as assignee and inventors         Weppner and Thangadurai, and which is herein incorporated by         reference:     -   Li_(5+x)A_(y)G_(z),M₂O₁₂ wherein     -   A is in each case independently a monovalent, divalent,         trivalent, or tetravalent cation (e.g. A is an alkaline earth         metal or transition metal such as Ca, Sr, Ba, Mg and/or Zn;     -   G is in each case independently a monovalent, divalent,         trivalent, or tetravalent cation (e.g. La);     -   M is in each case independently a trivalent, tetravalent, or         pentavalent cation; with 0<x≤3, 0<y≤3, and 0<z≤3 (e.g. a         transition metal such as Nb, Ta, Sb and V); and     -   O can be partially or completely replaced by divalent and/or         trivalent anions such as e.g. N³⁻; and furthermore,     -   within a structure of this formal composition L, A, G and M can         each be the same or different.     -   For example, Li_(5+x)A_(y)G_(3-x)M₂O₁₂ [such as Li₆ALa₂M₂O₁₂,         e.g., Li₆ALa₂Ta₂O₁₂ (A=Sr, Ba)]         (iv) garnet like compounds as described in U.S. Patent Pub. No.:         2011/0053002 having NGK Insulators, Ltd., as assignee and         inventors Yamamura, Hattori, Yoshida, Honda, and Sato, and which         is herein incorporated by reference, for instance a ceramic         material containing:     -   (a) Li, La, Zr, Nb, O; or (b) Li, La, Zr, Ta, O; or (c) Li, La,         Zr, Nb, Ta, O. For example, Li_(a)La_(b)Zr_(x)M_(y)O_(c) wherein         M represents the total number of moles of Nb and Ta, the molar         ratios of the constitutive metal elements containing Nb and Ta         can be set to be a:b:x+y:y=7:3:2:0.1 or greater to 0.6 or lower.         In addition the ceramic material may contain Al (e.g.,         Li_(a)La_(b)Zr_(x)M_(y)O_(c)zAl (wherein M represents the total         number of moles of Nb and Ta and the molar ratios of the         constitutive metal elements can be set to be         a:b:x+y:z=7:3:2:0.025 or greater to 0.35 or lower.         (v) garnet like compounds as described in U.S. Patent Pub. No.:         2010/0203383 having BASF SE, as assignee and inventor Werner         Weppner, and which is herein incorporated by reference, for         instance a compound having the general formula:     -   Li_(7+x)A_(x)G_(3-x)Zr₂O₁₂ wherein     -   A is in each case independently a divalent cation (or         combination of such cations, preferably divalent metal cations         such as alkaline earth metal ions such as Ca, Sr, Ba, and/or Mg         and also divalent cations such as Zn);     -   G is in each case independently a trivalent cation (or         combination of such cations, with preference given to La);     -   with 0≤x≤3 (and preference is given to 0≤x≤2 and in particular         0≤x≤1); and     -   O can be partly or completely replaced by divalent or trivalent         anions such as N³⁻         (vi) nasicon like compounds as described in U.S. Pat. No.         4,985,317 having Japan Synthetic Rubber Co., Ltd. as assignee         and inventors Adachi, Imanaka, Aono, Sugimoto, Sadaoka, Yasuda,         Hara, Nagata, and which is herein incorporated by reference, for         instance a compound (sometimes referred to as LTP) having the         general formula:     -   (a) Li_(1+x)M_(x)Ti_(2-x)(PO₄)₃ wherein     -   M is at least one element selected from the group consisting of         Fe, Al and rare earth elements and x is a number from 0.1 to         1.9; or     -   (b) Li_(1+y)Ti₂Si_(y)P_(3-y)O₁₂ wherein y is a number from 0.1         to 2.9; or     -   (c) or some combination of (a) and (b)         (vii) lithium ion conductive compounds having the following         composition:

Composition Mol % P₂O₅ 26 - 55%  SiO₂ 0 - 15% GeO₂ and TiO₂ 25 - 50%  in which TiO₂ 0 - 50% in which GeO₂ 0 - 50% ZrO₂ 0 - 10% M₂O₃ 0 < 10%  Al₂O₃ 0 - 15% Ga₂O₃ 0 - 15% Li₂O 3 - 25% And in particular lithium ion conductive compounds having the following general formula:

Li_(1+x)(M,Al,Ga)_(x)(Ge_(1-y)Ti_(y))_(2-x)(PO₄)₃ where x≤0.8 and 0≤x≤1.0 and where M is an element selected from the group consisting of Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm and Yb and/or Li_(1+x+y)Q_(x)Ti_(2-x)Si_(y)P_(3-y) O₁₂ where 0<x≤0.4 and 0<y≤0.6 and where Q is Al or Ga. For example Li_((1+x))Al_(x)Ti_(2-x)(PO₄)₃ where X is 0 to 0.8 as described in U.S. Pat. No. 5,702,995 having Kabushiki Kaisha Ohara as assignee and inventor Jie Fu, and which is herein incorporated by reference.

Other suitable materials include glassy or amorphous metal ion conductors, such as a phosphorus-based glass, oxide-based glass, phosphorus-oxynitride-based glass, sulpher-based glass, oxide/sulfide based glass, selenide based glass, gallium based glass, germanium-based glass, Nasiglass; ceramic active metal ion conductors, such as lithium beta-alumina, sodium beta-alumina, Li superionic conductor (LISICON), Na superionic conductor (NASICON), and the like; or glass-ceramic active metal ion conductors. Specific examples include LiPON, Li₃PO₄.Li₂S.SiS₂, Li₂S.GeS₂.Ga₂S₃, Li₂O.11Al₂O₃, Na₂O.11Al₂O₃, (Na,Li)_(1+x)Ti_(2-x)Al_(x)(PO₄)₃ (0.1≤x≤0.9) and crystallographically related structures, Li_(1+x)Hf_(2-x)Al_(x)(PO₄)₃ (0.1≤x≤0.9), Na₃Zr₂Si₂PO₁₂, Li₃Zr₂Si₂PO₁₂, Na₅ZrP₃O₁₂, Na₅TiP₃O₁₂, Na₃Fe₂P₃O₁₂, Na₄NbP₃O₁₂, Na-Silicates, Li_(0.3)La_(0.5)TiO₃, Na₅MSi₄O₁₂ (M: rare earth such as Nd, Gd, Dy) Li₅ZrP₃O₁₂, Li₅TiP₃O₁₂, Li₃Fe₂P₃O₁₂ and Li₄NbP₃O₁₂, and combinations thereof, optionally sintered or melted. Suitable ceramic ion active metal ion conductors are described, for example, in U.S. Pat. No. 4,985,317 to Adachi et al., incorporated by reference herein in its entirety and for all purposes.

A particularly suitable glass-ceramic material is a lithium ion conductive glass-ceramic having the following composition:

Composition mol % P₂O₅ 26-55%  SiO₂ 0-15% GeO₂ + TiO₂ 25-50%  in which GeO₂ 0-50% TiO₂ 0-50% ZrO₂ 0-10% M₂O₃ 0-10% Al₂O₃ 0-15% Ga₂O₃ 0-15% Li₂O 3-25% and/or such a material containing a predominant crystalline phase composed of Li_(1+x)(M,Al,Ga)_(x)(Ge_(1-y)Ti_(y))_(2-x)(PO₄)₃ where X=0.8 and 0=Y=1.0, and where M is an element selected from the group consisting of Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm and Yb and/or Li_(1+x+y)Q_(x)Ti_(2-x)Si_(y)P_(3-y)O₁₂ where 0<X=0.4 and 0<Y=0.6, and where Q is Al or Ga. The glass-ceramics are obtained by melting raw materials to a melt, casting the melt to a glass and subjecting the glass to a heat treatment. Such materials are available from OHARA Corporation, Japan and are further described in U.S. Pat. Nos. 5,702,995, 6,030,909, 6,315,881 and 6,485,622, incorporated herein by reference.

Suitable solid-state ion conductor materials for the membrane include Li₆BaLa₂Ta₂O₁₂; Li₇La₃Zr₂O₁₂, Li₅La₃Nb₂O₁₂, Li₅La₃M₂O₁₂ (M=Nb, Ta)Li_(7+x)A_(x)La_(3-x) Zr₂O₁₂ where A may be Zn or another transition metal. These materials and methods for making them are described in U.S. Patent Application Pub. No.: 2007/0148533 (application Ser. No. 10/591,714) and is hereby incorporated by reference in its entirety and suitable garnet like structures, are described in International Patent Application Pub. No.: WO/2009/003695, herein incorporated by reference for all that it contains.

The garnet structure can be modified by doping different elements so enhance performance such as chemical compatibility, ease of fabrication, reducing cost, and increasing conductivity. Particularly suitable substantially impervious garnet like layers include modified garnet like layers having compositions of about Li₆SrLa₂Ta₂O₁₂, Li₆BaLa₂Ta₂O₁₂, Li₆CaLa₂Nb₂O₁₂, Li₆SrLa₂Nb₂O₁₂, Li₆BaLa₂Nb₂O₁₂, Li₅La₃Bi₂O₁₂, Li₆SrLa₂Bi₂O₁₂, Li₅La₃Nb_(1.9)Y_(0.1)O12, Li₇La₃Hf₂O₁₂, Li_(6.55)La₃Hf_(1.55)Ta_(0.45)O₁₂, Li₅Nd₃Sb₂O₁₂, Li₇La₃Sn₂O₁₂, Li₇La₃Zr₂O₁₂, Li_(6.75)La₃Zr_(1.75)Nb_(0.25)O₁₂, Li_(6.25)La₃Zr₂Ga_(0.25)O₁₂, Li₇La₃Zr₂O₁₂ (LLZO) doped with Ge, Si, In, Al or some combination thereof

Referring to FIG. 1, a specific embodiment of the present invention is illustrated and described. FIG. 1 shows an unscaled depiction of an electrochemical cell structure 100 having an active metal, active metal-ion, active metal alloying metal, or active metal intercalating material anode 102 and an ionically conductive protective architecture 104. The protective architecture 104 has an active metal ion conducting separator layer 106 with a non-aqueous anolyte (sometimes also referred to as a transfer electrolyte) on a surface of the anode 102 and a substantially impervious ionically conductive layer 108 in contact with the separator layer 106. The separator layer 106 is chemically compatible with the active metal and the substantially impervious layer 108 is chemically compatible with the separator layer 106 and aqueous environments. The structure 100 may optionally include a current collector 110, composed of a suitable conductive metal that does not alloy with or intercalate the active metal. When the active metal is lithium, a suitable current collector material is copper. The current collector 110 can also serve to seal the anode from ambient to prevent deleterious reaction of the active metal with ambient air or moisture.

In various embodiments the separator layer 106 is composed of a porous membrane impregnated with a non-aqueous anolyte. For example, the membrane may be a micro-porous polymer, such as are available from Celgard, Inc. The non-aqueous anolyte may be in the liquid or gel phase. For example, the anolyte may include a solvent selected from the group consisting of organic carbonates, ethers, lactones, sulfones, etc, and combinations thereof, such as EC, PC, DEC, DMC, EMC, 1,2-DME or higher glymes, THF, 2MeTHF, sulfolane, ionic liquids (as are known in the art) and combinations thereof. 1,3-dioxolane may also be used as an anolyte solvent, particularly but not necessarily when used to enhance the safety of a cell incorporating the structure, as described further below. Generally the anolyte should be chemically compatible in contact with the active metal anode, and in this regard may include compatible liquid solvents (i.e., those which are solely compatible) as well as those solvents which are not compatible by themselves but in combination with a suitable electrolytic salt and/or additional solvent(s) leads to a chemically compatible anolyte. Such liquid solvents (solely chemically compatible or otherwise) may include organic or inorganic solvents such as those described above, as well as ionic liquid solvents. For instance the chemically compatible anolyte may be composed of an ionic liquid in combination with non-aqueous organic liquid solvent(s) and an optional salt. When the anolyte is in the gel phase, gelling agents such as polyvinylidine fluoride (PVdF) compounds, hexafluropropylene-vinylidene fluoride copolymers (PVdf-HFP), polyacrylonitrile compounds, cross-linked polyether compounds, polyalkylene oxide compounds, polyethylene oxide compounds, and combinations and the like may be added to gel the solvents. Suitable anolytes will also, of course, also include active metal salts, such as, in the case of lithium, for example, LiPF₆, LiBF₄, LiAsF₆, LiSO₃CF₃ or LiN(SO₂C₂F₅)₂. One example of a suitable separator layer is 1 M LiPF₆ dissolved in propylene carbonate and impregnated in a Celgard microporous polymer membrane.

When the anolyte is in the gel phase it may be used as a freestanding layer or otherwise as a coating on the lithium metal or on the substantially impervious layer. Both organic solvent- and ionic liquid-based gels as well as combinations thereof are contemplated for use herein as an interlayer.

As described in U.S. Pat. No. 8,332,028, other anolyte solvents including ionic liquids, and especially non-aqueous organic ionic liquids, as well as inorganic ionic liquids which are sufficiently compatible in contact with the lithium anode layer (e.g., lithium metal or lithium intercalation material, such as carbon) may be used as anolyte herein. Ionic liquids are a subclass of non-aqueous solvents and are generally known in the battery art for their use as an electrolyte component. Ionic liquids generally suitable for use herein are preferably liquids at room temperature, although the invention is not limited as such, and organic salts having melting points below 100° C. are generally contemplated. Ionic liquids are known in the art, including those based on imidazolium and pyrrolidinium. The ionic liquids will generally contain a lithium salt, such as those having a TFSI anion.

As a particular type of non-aqueous electrolyte, ionic liquid based electrolytes may be impregnated in a porous membrane (e.g., a microporous membrane) or caused to swell or gel a polymeric separator material. Typically, the ionic liquid will further comprise a lithium salt dissociated therein to provide charge carriers. In some instances the ionic liquid may be caused to polymerize, and in such instances, the polymeric ionic liquid may itself serve as the lithium ion conducting separator layer. Ionic liquid based electrolytes, including those which are caused to swell or gel a polymeric separator layer (e.g., polyvinylidene fluoride [PVdF] or poly-ethylene oxide [PEO]) are suitable for use herein and are known in the art. Ionic liquids may be classified according to their cation and anion compositions. For example ionic liquid cations which are known in the art include those of the Pyrrolidinium type (e.g., N-methyl-N-propylpyrrolidinium, N-propyl-N-methylpyrrolidinium [PYR13+], 1-butyl-1-methylpyrrolidinium [PYR14+], Imidazolium (e.g., 1-ethyl-3-methylimidazolium [EMI+]). For example ionic liquid anions which are known in the art include those of the type bis(trifluoromethanesulfonyl)imide and bis(fluorosulfonyl)imide. A particularly suitable lithium salt is that of the type lithium bis(trifluoromethanesulfonyl)imide. For example, N-Butyl-N-methylpyrrolidinium bis(trifluoromethanesulfonyl)imide [PYR14TFSI] and N-Butyl-N-methylpyrrolidinium bis(fluorosulfonyl)imide [PYR14FSI] impregnated in a porous separator or caused to gel or swell a suitable polymer such as PEO or PVdF, and having dissolved therein the lithium salt LiTFSI. It should be understand to one of skill in the art that the search for new and improved ionic liquid based electrolytes (or electrolytes comprising ionic liquids) for use in lithium batteries is an ongoing worldwide effort, and thus it is contemplated herein that novel and hitherto unknown ionic liquids suitable for use herein as an anolyte will be discovered, and especially those having improved stability against electroactive lithium materials such as lithium metal, and thus will provide particular benefit, and by this expedient such ionic liquids are contemplated herein for use as an anolyte of the instant protected anode.

Another suitable anolyte includes a solution of a non-aqueous solvent(s) combined with a very high concentration of a lithium salt (e.g., about an equimolar complex of liquid solvent with lithium salts); for example, an about equimolar complex of a glyme (e.g., tri-glyme or tetra-glyme) and a lithium salt of lithium bis(trifluoromethanesulfonyl)amide [LiTFSA] or other such as lithium bis(trifluoromethanesulfonyl)imide LiTFSI or lithium bis(fluorosulfonyl)imide. This anolyte may behave like a concentrated solution or an ionic liquid. In some embodiments, fumed silica or other high surface area particles may be added to the solution to enhance solution properties and in some instances for making the solution behave like a semi-solid.

In various embodiments the anolyte may be in the gel phase or the anolyte may be a liquid anolyte swelled in or by a polymer layer. Such embodiments contemplate gel phase anolytes of non-aqueous organic or ionic liquid solvents typically in combination with a salt, or combinations thereof of a gel phase anolyte comprising both a non-aqueous organic liquid solvent and a suitable ionic liquid solvent as described above.

There are a number of advantages of a protective architecture in accordance with the present invention. In particular, cell structures incorporating such an architecture may be relatively easily manufactured. In one example, lithium metal is simply placed against a micro-porous separator impregnated with organic liquid or gel electrolyte and with the separator adjacent to a glass/glass ceramic active metal ion conductor.

An additional advantage of the non-aqueous interlayer is realized when glass-ceramics are used. When amorphous glasses of the type described by the OHARA Corp. patents cited above are heat-treated, the glass devitrifies, leading to the formation of a glass-ceramic. However, this heat treatment can lead to the formation of surface roughness which may be difficult to coat using vapor phase deposition of an inorganic protective interlayer such as LiPON, Cu₃N, etc. The use of a liquid (or gel), non-aqueous electrolyte interlayer would easily cover such a rough surface by normal liquid flow, thereby eliminating the need for surface polishing, etc. In this sense, techniques such as “draw-down” (as described by Sony Corporation and Shott Glass (T. Kessler, H. Wegener, T. Togawa, M. Hayashi, and T. Kakizaki, “Large Microsheet Glass for 40-in. Class PALC Displays,” 1997, FMC2-3, incorporated herein by reference) could be used to form thin glass layers (20 to 100 microns), and these glasses heat treated to form glass-ceramics.

In yet other embodiments, the interlayer may be integrated with the second material layer (i.e., the substantially impervious layer). For instance, the second material layer may be a sintered layer of a glass, ceramic or glass ceramic and the porous interlayer integrated therewith. For example, the porous interlayer composed of a substantially similar composition and/or crystal structure as that of the second material layer (e.g., an anode compatible LTP composition or Garnet like material) except that the integrated interlayer is porous and therefore accepting of a liquid phase anolyte. For instance, the integrated structure may be fabricated by tape casting of a multi-layer (e.g., a dual layer) wherein at least one of the layers is substantially impervious and the layer opposing the anode (e.g., in direct contact) is porous. In some embodiments, the integrated structure may be further paired with an additional porous interlayer which separates the integrated layer from the anode and by this expedient allows for the use of an anode incompatible integrated structure into the protective architecture.

In other embodiments, it is contemplated that the substantially impervious layer may be formed on or in conjunction with an electronically insulating and ionically insulating porous substrate as a support layer. The substantially impervious layer may be fabricated as a coating or film on the porous support (e.g., the porous support composed of a rigid glass or polycrystalline ceramic or glass-ceramic), or it may be fabricated using multi-layer tape casting wherein one or more layers are lithium ion conductors and one or more other layers provide a porous, non-conducting support.

In addition, porous metal support layer embodiments are also contemplated. Generally when a porous metal support is used it may be positioned on the surface that opposes the external environment about the protected anode (e.g., that side which opposes the cathode). However, this embodiment is not limited as such and the porous metal support may oppose the anode, but in such embodiments an insulating generally porous polymeric separator may be incorporated between the porous metal layer and the lithium layer, for the purpose of providing electronic isolation therebetween.

In yet a further embodiment, the interlayer may effectively be provided by a gap (i.e., a space) which contains a liquid phase anolyte but no material interlayer. The gap may be incorporated in the anode structure using any number of suitable constructions, including wherein the substantially impervious membrane is attached to a frame (e.g., provided by the battery casing) at a spaced apart distance from the lithium metal layer, and the gap subsequently created there between the layers filled with liquid anolyte. In other words a liquid anolyte interlayer devoid of a porous solid material layer is contemplated herein.

Battery Cells

The non-aqueous interlayer architecture is usefully adopted in battery cells. For example, the electrochemical structure 100 of FIG. 1 can be paired with a cathode system 120 to form a cell 200, as depicted in FIG. 2. The cathode system 120 includes an electronically conductive component, an ionically conductive component, and an electrochemically active component. The cathode system 120 may have any desired composition and, due to the isolation provided by the protective architecture, is not limited by the anode or anolyte composition. In particular, the cathode system may incorporate components which would otherwise be highly reactive with the anode active metal, such as aqueous materials, including water, aqueous catholytes and air, metal hydride electrodes and metal oxide electrodes.

In one embodiment, a Celgard separator would be placed against one side of the thin glass-ceramic, followed by a non-aqueous liquid or gel electrolyte, and then a lithium electrode. On the other side of the glass ceramic membrane, an aggressive solvent could be used, such as an aqueous electrolyte. In such a way, an inexpensive Li/water or Li/air cell, for example, could be built.

Cathode Systems

As noted above, the cathode system 120 of a battery cell in accordance with the present invention may have any desired composition and, due to the isolation provided by the protective architecture, is not limited by the anode or anolyte composition. In particular, the cathode system may incorporate components which would otherwise be highly reactive with the anode active metal, such as aqueous materials, including water, aqueous solutions and air, metal hydride electrodes and metal oxide electrodes.

Battery cells of the present invention may include, without limitation, water, aqueous solutions, air electrodes and metal hydride electrodes, such as are described in co-pending application Ser. No. 10/772,157 titled ACTIVE METAL/AQUEOUS ELECTROCHEMICAL CELLS AND SYSTEMS, now U.S. Pat. No. 7,645,543, incorporated herein by reference in its entirety and for all purposes, and metal oxide electrodes, as used, for example, in conventional Li-ion cells.

The effective isolation between anode and cathode achieved by the protective interlayer architecture of the present invention also enables a great degree of flexibility in the choice of catholyte systems, in particular aqueous systems, but also non-aqueous systems. Since the protected anode is completely decoupled from the catholyte, so that catholyte compatibility with the anode is no longer an issue, solvents and salts which are not kinetically stable to Li can be used.

For cells using water as an electrochemically active cathode material, a porous electronically conductive support structure can provide the electronically conductive component of the cathode system. An aqueous electrolyte (catholyte) provides ion carriers for transport (conductivity) of Li ions and anions that combine with Li. The electrochemically active component (water) and the ionically conductive component (aqueous catholyte) will be intermixed as a single solution, although they are conceptually separate elements of the battery cell. Suitable catholytes for the Li/water battery cell of the invention include any aqueous electrolyte with suitable ionic conductivity. Suitable electrolytes may be acidic, for example, strong acids like HCl, H₂SO₄, H₃PO₄ or weak acids like acetic acid/Li acetate; basic, for example, LiOH; neutral, for example, sea water, LiCl, LiBr, LiI; or amphoteric, for example, NH₄Cl, NH₄Br, etc

The suitability of sea water as an electrolyte enables a battery cell for marine applications with very high energy density. Prior to use, the cell structure is composed of the protected anode and a porous electronically conductive support structure (electronically conductive component of the cathode). When needed, the cell is completed by immersing it in sea water which provides the electrochemically active and ionically conductive components. Since the latter components are provided by the sea water in the environment, they need not transported as part of the battery cell prior to it use (and thus need not be included in the cell's energy density calculation). Such a cell is referred to as an “open” cell since the reaction products on the cathode side are not contained. Such a cell is, therefore, a primary cell.

Secondary Li/water cells are also possible in accordance with the invention. As noted above, such cells are referred to as “closed” cells since the reaction products on the cathode side are contained on the cathode side of the cell to be available to recharge the anode by moving the Li ions back across the protective membrane when the appropriate recharging potential is applied to the cell.

As noted above and described further below, in another embodiment of the invention, ionomers coated on the porous catalytic electronically conductive support reduce or eliminate the need for ionic conductivity in the electrochemically active material.

The electrochemical reaction that occurs in a Li/water cell is a redox reaction in which the electrochemically active cathode material gets reduced. In a Li/water cell, the catalytic electronically conductive support facilitates the redox reaction. As noted above, while not so limited, in a Li/water cell, the cell reaction is believed to be: Li+H₂O=LiOH+½H₂. The half-cell reactions at the anode and cathode are believed to be: Li=Li⁺ +e ⁻  Anode: e ⁻+H₂O=OH⁻+½H₂  Cathode:

Accordingly, the catalyst for the Li/water cathode promotes electron transfer to water, generating hydrogen and hydroxide ion. A common, inexpensive catalyst for this reaction is nickel metal; precious metals like Pt, Pd, Ru, Au, etc. will also work but are more expensive.

Also considered to be within the scope of Li (or other active metal)/water batteries of this invention are batteries with a protected Li anode and an aqueous electrolyte composed of gaseous and/or solid oxidants soluble in water that can be used as active cathode materials (electrochemically active component). Use of water soluble compounds, which are stronger oxidizers than water, can significantly increase battery energy in some applications compared to the lithium/water battery, where during the cell discharge reaction, electrochemical hydrogen evolution takes place at the cathode surface. Examples of such gaseous oxidants are O₂, SO₂ and NO₂. Also, metal nitrites, in particular NaNO₂ and KNO₂ and metal sulfites such as Na₂SO₃ and K₂SO₃ are stronger oxidants than water and can be easily dissolved in large concentrations. Another class of inorganic oxidants soluble in water are peroxides of lithium, sodium and potassium, as well as hydrogen peroxide H₂O₂.

The use of hydrogen peroxide as an oxidant can be especially beneficial. There are at least two ways of utilizing hydrogen peroxide in a battery cell in accordance with the present invention. First of all, chemical decomposition of hydrogen peroxide on the cathode surface leads to production of oxygen gas, which can be used as active cathode material. The second, perhaps more effective way, is based on the direct electroreduction of hydrogen peroxide on the cathode surface. In principal, hydrogen peroxide can be reduced from either basic or acidic solutions. The highest energy density can be achieved for a battery utilizing hydrogen peroxide reduction from acidic solutions. In this case a cell with Li anode yields E⁰=4.82 V (for standard conditions) compared to E⁰=3.05 V for Li/Water couple. However, because of very high reactivity of both acids and hydrogen peroxide to unprotected Li, such cell can be practically realized only for protected Li anode such as in accordance with the present invention.

For cells using air as an electrochemically active cathode material, the air electrochemically active component of these cells includes moisture to provide water for the electrochemical reaction. The cells have an electronically conductive support structure electrically connected with the anode to allow electron transfer to reduce the air cathode active material. The electronically conductive support structure is generally porous to allow fluid (air) flow and either catalytic or treated with a catalyst to catalyze the reduction of the cathode active material. An aqueous electrolyte with suitable ionic conductivity or ionomer is also in contact with the electronically conductive support structure to allow ion transport within the electronically conductive support structure to complete the redox reaction.

The air cathode system includes an electronically conductive component (for example, a porous electronic conductor), an ionically conductive component with at least an aqueous constituent, and air as an electrochemically active component. It may be any suitable air electrode, including those conventionally used in metal (e.g., Zn)/air batteries or low temperature (e.g., PEM) fuel cells. Air cathodes used in metal/air batteries, in particular in Zn/air batteries, are described in many sources including “Handbook of Batteries” (Linden and T. B. Reddy, McGraw-Hill, NY, Third Edition) and are usually composed of several layers including an air diffusion membrane, a hydrophobic Teflon layer, a catalyst layer, and a metal electronically conductive component/current collector, such as a Ni screen. The catalyst layer also includes an ionically conductive component/electrolyte that may be aqueous and/or ionomeric. A typical aqueous electrolyte is composed of KOH dissolved in water. A typical ionomeric electrolyte is composed of a hydrated (water) Li ion conductive polymer such as a per-fluoro-sulfonic acid polymer film (e.g., du Pont NAFION). The air diffusion membrane adjusts the air (oxygen) flow. The hydrophobic layer prevents penetration of the cell's electrolyte into the air-diffusion membrane. This layer usually contains carbon and Teflon particles. The catalyst layer usually contains a high surface area carbon and a catalyst for acceleration of reduction of oxygen gas. Metal oxides, for example MnO₂, are used as the catalysts for oxygen reduction in most of the commercial cathodes. Alternative catalysts include metal macrocycles such as cobalt phthalocyanine, and highly dispersed precious metals such at platinum and platinum/ruthenium alloys. Since the air electrode structure is chemically isolated from the active metal electrode, the chemical composition of the air electrode is not constrained by potential reactivity with the anode active material. This can allow for the design of higher performance air electrodes using materials that would normally attack unprotected metal electrodes.

Another type of active metal/aqueous battery cell incorporating a protected anode and a cathode system with an aqueous component in accordance with the present invention is a lithium (or other active metal)/metal hydride battery. For example, lithium anodes protected with a non-aqueous interlayer architecture as described herein can be discharged and charged in aqueous solutions suitable as electrolytes in a lithium/metal hydride battery. Suitable electrolytes provide a source or protons. Examples include aqueous solutions of halide acids or acidic salts, including chloride or bromide acids or salts, for example HCl, HBr, NH₄Cl or NH₄Br.

In addition to the aqueous, air, etc., systems noted above, improved performance can be obtained with cathode systems incorporating conventional Li-ion battery cathodes and electrolytes, such as metal oxide cathodes (e.g., Li_(x)CoO₂, Li_(x)NiO₂, Li_(x)Mn₂O₄ and LiFePO₄) and the binary, ternary or multicomponent mixtures of alkyl carbonates or their mixtures with ethers as solvents for a Li metal salt (e.g., LiPF₆, LiAsF₆ or LiBF₄); or Li metal battery cathodes (e.g., elemental sulfur or polysulfides) and electrolytes composed of organic carbonates, ethers, glymes, lactones, sulfones, sulfolane, and combinations thereof, such as EC, PC, DEC, DMC, EMC, 1,2-DME, THF, 2MeTHF, and combinations thereof, as described, for example, in U.S. Pat. No. 6,376,123, incorporated herein by reference.

Moreover, the catholyte solution can be composed of only low viscosity solvents, such as ethers like 1,2-dimethoxy ethane (DME), tetrahydrofuran (THF), 2-methyltetrahydrofuran, 1,3-dioxolane (DIOX), 4-methyldioxolane (4-MeDIOX) or organic carbonates like dimethylcarbonate (DMC), ethylmethylcarbonate (EMC), diethylcarbonate (DEC), or their mixtures. Also, super low viscosity ester solvents or co-solvents such as methyl formate and methyl acetate, which are very reactive to unprotected Li, can be used. As is known to those skilled in the art, ionic conductivity and diffusion rates are inversely proportional to viscosity such that all other things being equal, battery performance improves as the viscosity of the solvent decreases. The use of such catholyte solvent systems significantly improves battery performance, in particular discharge and charge characteristics at low temperatures.

Ionic liquids may also be used in catholytes of the present invention. Ionic liquids are organic salts with melting points under 100 degrees, often even lower than room temperature. The most common ionic liquids are imidazolium and pyridinium derivatives, but also phosphonium or tetralkylammonium compounds are also known. Ionic liquids have the desirable attributes of high ionic conductivity, high thermal stability, no measurable vapor pressure, and non-flammability. Representative ionic liquids are 1-Ethyl-3-methylimidazolium tosylate (EMIM-Ts), 1-Butyl-3-methylimidazolium octyl sulfate (BMIM-OctSO4), 1-Ethyl-3-methylimidazolium hexafluorophosphate, and 1-Hexyl-3-methylimidazolium tetrafluoroborate. Although there has been substantial interest in ionic liquids for electrochemical applications such as capacitors and batteries, they are unstable to metallic lithium and lithiated carbon. However, protected lithium anodes as described in this invention are isolated from direct chemical reaction, and consequently lithium metal batteries using ionic liquids are possible as an embodiment of the present invention. Such batteries should be particularly stable at elevated temperatures.

Safety Additives

As a safety measure, the non-aqueous interlayer architecture can incorporate a gelling/polymerizing agent that, when in contact with the reactive electrolyte (for example water), leads to the formation of an impervious polymer on the anode (e.g., lithium) surface. This safety measure is used for the case where the substantially impervious layer of the protective architecture (e.g., a glass or glass-ceramic membrane) cracks or otherwise breaks down and allows the aggressive catholyte to enter and approach the lithium electrode raising the possibility of a violent reaction between the Li anode and aqueous catholyte.

Such a reaction can be prevented by providing in the anolyte a monomer for a polymer that is insoluble or minimally soluble in water, for example dioxolane (Diox) (for example, in an amount of about 5-20% by volume) and in the catholyte a polymerization initiator for the monomer, for example, a protonic acid. A Diox based anolyte may be composed of organic carbonates (EC, PC, DEC, DMC, EMC), ethers (1, 2-DME, THF, 2MeTHF, 1,3-dioxolane and others) and their mixtures. Anolyte comprising dioxolane as a main solvent (e.g., 50-100% by volume) and Li salt, in particular, LiAsF₆, LiBF₄, LiSO₃CF₃, LiN(SO₂C₂F₅)₂, is especially attractive. Diox is a good passivating agent for Li surface, and good cycling data for Li metal has been achieved in the Diox based electrolytes (see, e.g., U.S. Pat. No. 5,506,068). In addition to its compatibility with Li metal, Diox in combination with above-mentioned ionic salts forms highly conductive electrolytes. A corresponding aqueous catholyte contains a polymerization initiator for Diox that produces a Diox polymerization product (polydioxolane) that is not or is only minimally soluble in water.

If the membrane breaks down, the catholyte containing the dissolved initiator comes in direct contact with the Diox based anolyte, and polymerization of Diox occurs next to the Li anode surface. Polydioxolane, which is a product of Diox polymerization, has high resistance, so the cell shuts down. In addition, the Polydioxolane layer formed serves as a barrier preventing reaction between the Li surface and the aqueous catholyte. Diox can be polymerized with protonic acids dissolved in the catholyte. Also, the water soluble Lewis acids, in particular benbenzoyl cation, can serve this purpose.

Thus, improvement in cyclability and safety is achieved by the use of a dioxolane (Diox) based anolyte and a catholyte containing a polymerization initiator for Diox.

Active Metal Ion and Alloy Anodes

The invention pertains to batteries and other electrochemical structures having anodes composed of active metals, as described above. A preferred active metal electrode is composed of lithium (Li). Suitable anolytes for these structures and cells are described above.

The invention also pertains to electrochemical structures having active metal ion (e.g., lithium-carbon) or active metal alloy (e.g., Li—Sn) anodes. Some structures may initially have uncharged active metal ion intercalation materials (e.g., carbon) or alloying metals (e.g., tin (Sn)) that are subsequently charged with active metal or active metal ions. While the invention may be applicable to a variety of active metals, it is described herein primarily with reference to lithium, as an example.

Carbon materials commonly used in conventional Li-ion cells, in particular petroleum coke and mesocarbon microbead carbons, can be used as anode materials in Li-ion aqueous battery cells. Lithium alloys comprising one or several of the metals selected from the group including Ca, Mg, Sn, Ag, Zn, Bi, Al, Cd, Ga, In and Sb, preferably Al, Sn or Si, can also be used as anode materials for such a battery. In one particular embodiment the anode comprises Li, Cu and Sn.

Anolyte for such structures can incorporate supporting salts, for example, LiAsF₆, LiClO₄, LiSO₃CF₃, LiN(CF₃SO₂)₂ or LiN(SO₂C₂F₅)₂ dissolved in binary or ternary mixtures of non-aqueous solvents, for example, EC, PC, DEC, DMC, EMC, MA, MF, commonly used in conventional Li-ion cells. Gel-polymer electrolytes, for instance electrolytes comprising one of the above mentioned salts, a polymeric binder, such as PVdF, PVdF-HFP copolymer, PAN or PEO, and a plasticizer (solvent) such as EC, PC, DEC, DMC, EMC, THF, 2MeTHF, 1,2-DME and their mixtures, also can be used.

For batteries using these anodes, a suitable cathode structure may be added to the electrochemical structure on the other side of the protective architecture. The architecture enables Li-ion type cells using a number of exotic cathodes such as air, water, metal hydrides or metal oxides. For Li-ion aqueous battery cells, for example, aqueous catholyte can be basic, acidic or neutral and contains Li cations. One example of a suitable aqueous catholyte is 2 M LiCl, 1 M HCl.

During the first charge of the battery with lithium-carbon lithium alloy anode, Li cations are transported from the catholyte through the protective architecture (including the anolyte) to the anode surface where the intercalation process takes place as in conventional Li-ion cells. In one embodiment, the anode is chemically or electrochemically lithiated ex-situ before cell assembly.

Cell Designs

Electrochemical structures and battery cells in accordance with the present invention may have any suitable geometry. For example, planar geometries may be achieved by stacking planar layers of the various components of the structures or cells (anode, interlayer, cathode, etc.) according to known battery cell fabrication techniques that are readily adaptable to the present invention given the description of the structure or cell components provided herein. These stacked layers may be configured as prismatic structures or cells.

Alternatively, the use of tubular glass or glass-ceramic electrolytes with a non-aqueous interlayer architecture allows for the construction of high surface area anodes with low seal area. As opposed to flat-plate design where the seal length increases with cell surface area, tubular construction utilizes an end seal where the length of the tube can be increased to boost surface area while the seal area is invariant. This allows for the construction of high surface area Li/water and Li/air cells that should have correspondingly high power density.

The use of a non-aqueous interlayer architecture in accordance with the present invention facilitates construction. An open-ended (with a seal) or close-ended glass or glass-ceramic (i.e., substantially impervious active metal ion conductive solid electrolyte) tube is partially filled with a non-aqueous organic electrolyte (anolyte or transfer electrolyte) as described above, for example such as is typically used in lithium primary batteries A lithium metal rod surrounded by some type of physical separator (e.g., a semi-permeable polymer film such as Celgard, Tonin, polypropylene mesh, etc.) having a current collector is inserted into the tube. A simple epoxy seal, glass-to-metal seal, or other appropriate seal is used to physically isolate the lithium from the environment.

The protected anode can then be inserted in a cylindrical air electrode to make a cylindrical cell, as shown in FIG. 3A. Or an array of anodes might be inserted into a prismatic air electrode, as shown in FIG. 3B.

This technology can also be used to build Li/water, Li/metal hydride or Li/metal oxide cells by substituting the air electrode with suitable aqueous, metal hydride or metal oxide cathode systems, as described herein above.

In addition to the use of lithium metal rods or wires (in capillary tubes), this invention can also be used to isolate a rechargeable LiC_(x) anode from aqueous or otherwise corrosive environments. In this case, appropriate anolyte (transfer electrolyte) solvents are used in the tubular anode to form a passive film on the lithiated carbon electrode. This would allow the construction of high surface area Li-ion type cells using a number of exotic cathodes such as air, water, metal hydrides or metal oxides, for example, as shown in FIG. 3C.

EXAMPLES

The following examples provide details illustrating advantageous properties of Li metal and Li-ion aqueous battery cells in accordance with the present invention. These examples are provided to exemplify and more clearly illustrate aspects of the present invention and in no way intended to be limiting.

Example 1: Li/Seawater Cell

A series of experiments was performed in which the commercial ionically conductive glass-ceramic from OHARA Corporation was used as a membrane separating aqueous catholyte and non-aqueous anolyte. The cell structure was Li/non-aqueous electrolyte/glass-ceramic/aqueous electrolyte/Pt. A lithium foil from Chemetall Foote Corporation with thickness of 125 microns was used as the anode. The GLASS-CERAMIC plates were in the range of 0.3 to 0.48 mm in thickness. The GLASS-CERAMIC plate was fitted into an electrochemical cell by use of two o-rings such that the GLASS-CERAMIC plate was exposed to an aqueous environment from one side and a non-aqueous environment from the other side. In this case, the aqueous electrolyte comprised an artificial seawater prepared with 35 ppt of “Instant Ocean” from Aquarium Systems, Inc. The conductivity of the seawater was determined to be 4.5 10⁻² S/cm. A microporous Celgard separator placed on the other side of the GLASS-CERAMIC was filled with non-aqueous electrolyte comprised of 1 M LiPF₆ dissolved in propylene carbonate. The loading volume of the nonaqueous electrolyte was 0.25 ml per 1 cm² of Li electrode surface. A platinum counter electrode completely immersed in the sea water catholyte was used to facilitate hydrogen reduction when the battery circuit was completed. An Ag/AgCl reference electrode was used to control potential of the Li anode in the cell. Measured values were recalculated into potentials in the Standard Hydrogen Electrode (SHE) scale. An open circuit potential (OCP) of 3.05 volts corresponding closely to the thermodynamic potential difference between Li/Li⁺ and H₂/H⁺ in water was observed (FIG. 4). When the circuit was closed, hydrogen evolution was seen immediately at the Pt electrode, which was indicative of the anode and cathode electrode reactions in the cell, 2Li=2Li+2e⁻ and 2H⁺+2e⁻=H₂. The potential-time curve for Li anodic dissolution at a discharge rate of 0.3 mA/cm² is presented in FIG. 2. The results indicate an operational cell with a stable discharge voltage. It should be emphasized that in all experiments using a Li anode in direct contact with seawater utilization of Li was very poor, and such batteries could not be used at all at low and moderate current densities similar to those used in this example due to the extremely high rate of Li corrosion in seawater (over 19 A/cm²).

Example 2: Li/Air Cell

The cell structure was similar to that in the previous example, but instead of a Pt electrode completely immersed in the electrolyte, this experimental cell had an air electrode made for commercial Zn/Air batteries. An aqueous electrolyte used was 1 M LiOH. A Li anode and a non-aqueous electrolyte were the same as described in the previous example.

An open circuit potential of 3.2 V was observed for this cell. FIG. 5 shows discharge voltage-time curve at discharge rate of 0.3 mA/cm². The cell exhibited discharge voltage of 2.8-2.9 V. for more than 14 hrs. This result shows that good performance can be achieved for Li/air cells with solid electrolyte membrane separating aqueous catholyte and non-aqueous anolyte.

Example 3: Li-Ion Cell

In these experiments the commercial ionically conductive glass-ceramic from OHARA Corporation was used as a membrane separating aqueous catholyte and non-aqueous anolyte. The cell structure was carbon/non-aqueous electrolyte/glass-ceramic plate/aqueous electrolyte/Pt. A commercial carbon electrode on copper substrate comprising a synthetic graphite similar to carbon electrodes commonly used in lithium-ion batteries was used as the anode. The thickness of the glass-ceramic plate was 0.3 mm. The glass-ceramic plate was fitted into an electrochemical cell by use of two o-rings such that the glass-ceramic plate was exposed to an aqueous environment from one side and a non-aqueous environment from the other side. The aqueous electrolyte comprised 2 M LiCl and 1 M HCl. Two layers of microporous Celgard separator placed on the other side of the glass-ceramic were filled with non-aqueous electrolyte comprised of 1 M LiPF₆ dissolved in the mixture of ethylene carbonate and dimethyl carbonate (1:1 by volume). A lithium wire reference electrode was placed between two layers of Celgard separator in order to control the potential of the carbon anode during cycling. A platinum mesh completely immersed in the 2 M LiCl, 1 M HCl solution was used as the cell cathode. An Ag/AgCl reference electrode placed in the aqueous electrolyte was used to control potential of the carbon electrode and voltage drop across the GLASS-CERAMIC plate, as well as potential of the Pt cathode during cycling. An open circuit voltage (OCV) around 1 volt was observed for this cell. The voltage difference of 3.2 volts between Li reference electrode and Ag/AgCl reference electrode closely corresponding to the thermodynamical value was observed. The cell was charged at 0.1 mA/cm² until the carbon electrode potential reached 5 mV vs. Li reference electrode, and then at 0.05 mA/cm² using the same cutoff potential. The discharge rate was 0.1 mA/cm², and discharge cutoff potential for the carbon anode was 1.8 V vs. Li reference electrode. The data in FIG. 6 show that the cell with intercalation carbon anode and aqueous electrolyte containing Li cations can work reversibly. This is the first known example where aqueous solution has been used in Li-ion cell instead of solid lithiated oxide cathode as a source of Li ions for charging of the carbon anode.

Alternative Embodiment—Li/Water Battery and Hydrogen Generator for Fuel Cell

The use of protective architecture on active metal electrodes in accordance with the present invention allows the construction of active metal/water batteries that have negligible corrosion currents, described above. The Li/water battery has a very high theoretical energy density of 8450 Wh/kg. The cell reaction is Li+H₂O=LiOH+½ H₂. Although the hydrogen produced by the cell reaction is typically lost, in this embodiment of the present invention it is used to provide fuel for an ambient temperature fuel cell. The hydrogen produced can be either fed directly into the fuel cell or it can be used to recharge a metal hydride alloy for later use in a fuel cell. At least one company, Millenium Cell, makes use of the reaction of sodium borohydride with water to produce hydrogen. However, this reaction requires the use of a catalyst, and the energy produced from the chemical reaction of NaBH₄ and water is lost as heat. NaBH₄+2H₂O→4H₂+NaBO₂

When combined with the fuel cell reaction, H₂+O₂=H₂O, the full cell reaction is believed to be: NaBH₄+20₂→2H₂O+NaBO₂

The energy density for this system can be calculated from the equivalent weight of the NaBH₄ reactant (38/4=9.5 grams/equiv.). The gravimetric capacity of NaBH₄ is 2820 mAh/g; since the voltage of the cell is about 1, the specific energy of this system is 2820 Wh/kg. If one calculates the energy density based on the end product NaBO₂, the energy density is lower, about 1620 Wh/kg.

In the case of the Li/water cell, the hydrogen generation proceeds by an electrochemical reaction believed described by: Li+H₂O=LiOH+½H₂

In this case, the energy of the chemical reaction is converted to electrical energy in a 3 volt cell, followed by conversion of the hydrogen to water in a fuel cell, giving an overall cell reaction believed described by: Li+½H₂O+¼O₂=LiOH where all the chemical energy is theoretically converted to electrical energy. The energy density based on the lithium anode is 3830 mAh/g at a cell potential of about 3 volts which is 11,500 Wh/kg (4 times higher than NaBH₄). If one includes the weight of water needed for the reaction, the energy density is then 5030 Wh/kg. If the energy density is based on the weight of the discharge product, LiOH, it is then 3500 Wh/kg, or twice the energy density of the NaBO₂ system. This can be compared to previous concepts where the reaction of lithium metal with water to produce hydrogen has also been considered. In that scenario the energy density is lowered by a factor of three, since the majority of the energy in the Li/H₂O reaction is wasted as heat, and the energy density is based on a cell potential for the H₂/O₂ couple (as opposed to 3 for Li/H₂O) which in practice is less than one. In this embodiment of the present invention, illustrated in FIG. 7, the production of hydrogen can also be carefully controlled by load across the Li/water battery, the Li/water battery has a long shelf life due to the protective membrane, and the hydrogen leaving the cell is already humidified for use in the H₂/air fuel cell.

CONCLUSION

Although the foregoing invention has been described in some detail for purposes of clarity of understanding, it will be apparent that certain changes and modifications may be practiced within the scope of the invention. In particular, while the invention is primarily described with reference to a lithium metal, alloy or intercalation anode, the anode may also be composed of any active metal, in particular, other alkali metals, such as sodium. It should be noted that there are many alternative ways of implementing both the process and compositions of the present invention. Accordingly, the present embodiments are to be considered as illustrative and not restrictive, and the invention is not to be limited to the details given herein.

All references cited herein are incorporated by reference for all purposes. 

What is claimed is:
 1. A battery cell comprising: a cathode comprising seawater; and a protected lithium metal electrode comprising a lithium anode and a protective architecture, the protective architecture comprising a first lithium ion conducting separator layer and a second lithium ion conducting layer; wherein the first layer further comprises a lithium ion conducting anolyte, and the second layer is a substantially impervious layer that prevents the lithium anode from deleterious reaction in direct contact with the seawater of the cathode.
 2. The battery cell of claim 1 wherein the lithium anode is lithium metal.
 3. The battery cell of claim 1 wherein the lithium anode comprises intercalating carbon.
 4. The battery cell of claim 1 wherein the lithium anode comprises a lithium alloying material.
 5. The battery cell of claim 4 wherein the lithium alloying material is silicon or tin.
 6. The battery cell of claim 1 wherein the anolyte is a liquid electrolyte.
 7. The battery cell of claim 1 wherein the anolyte is a gel electrolyte.
 8. The battery cell of claim 1 wherein the anolyte is a polymer electrolyte.
 9. The battery cell of claim 1 wherein the first separator layer further comprises glass or ceramic particles.
 10. The battery cell of claim 9 wherein the glass or ceramic particles getter shorting dendrites.
 11. The battery cell of claim 1 wherein the lithium ion conducting substantially impervious second layer directly contacts the seawater of the cathode.
 12. The battery cell of claim 1 wherein the substantially impervious second material layer is a tape cast layer.
 13. The battery cell of claim 12 wherein the tape cast layer comprises a garnet lithium ion conductor.
 14. The battery cell of claim 1 wherein the second material layer comprises a garnet lithium ion conductor.
 15. The battery cell of claim 1 wherein the second material layer comprises a ceramic lithium ion conductor comprising lithium titanium phosphate.
 16. The battery cell of claim 12 wherein the second material layer comprises a ceramic lithium ion conductor comprising lithium titanium phosphate. 